 石英粒 |
|
|
|
Purity |
99.993% |
|
| |
| 矽(硅)塊 |
|
Purity |
≥99.9999% |
| Size |
25mm-250mm |
| Type |
P |
| Resistivity |
≧100 ohm.cm |
|
| |
| 矽(硅)晶棒 |
|
Size |
6” |
8” |
| Type/ Dopant |
P/ Boron |
P/ Boron |
| Growing Method |
CZ |
CZ |
| Orientation |
<100> ±2° |
<100> ±2° |
| Diameter |
153.0 ±1 mm |
203.0±1 mm |
| Lifetime |
>10 us |
>10 us |
| Resistivity |
0.5-6.0 ohm.cm |
0.5-6.0 ohm.cm |
| Oxygen content |
|
|
| Carbon content |
|
|
|
| |
| 矽(硅)晶片 |
| • 單矽(硅)晶片 |
|
Size |
6” |
8” |
| Type |
P |
P |
| Length |
125*125 mm |
156*156mm |
| Resistivity |
0.5-3.0 (3.0-6.0) ohm.cm |
0.5-3.0 (3.0-6.0) ohm.cm |
| Oxygen content |
|
|
| Carbon content |
|
|
| Thickness |
220±20μm |
240±20μm |
|
| |
| • 多矽(硅)晶片 |
|
Size |
6” |
8” |
| Type |
P |
P |
| Length |
125*125±0.5 mm |
156*156±0.5 mm |
| Resistivity |
0.5-3.0 (3.0-6.0) ohm.cm |
0.5-3.0 (3.0-6.0) ohm.cm |
| Oxygen content |
|
|
| Carbon content |
|
|
| Thickness |
220±20μm |
220±20μm |
|
| |
| 碎片 |
|
| |
| 頭、尾料 |
|
| |
| 矽(硅)粉 |
|
Purity |
11N |
| Type |
P |
| Resistivity |
≥0.5 ohm.cm |
| Original |
Japan |
|
| |
| |
| |